Makrolon ET3137

MVR (300 °C/1.2 kg) 6.0 cm³/10 min; Extrusion; high viscosity; branched; UV stabilized; easy release; multi wall sheets / profiles; panels

Makrolon ET3137基本性能(23°C)

属性名称 测试标准 测试标准 单位 数值

吸水性 （饱和值） ISO 62 Water at 23 °C % 0.3

吸水性（静态均衡值） ISO 62 23 °C; 50 % r. h. % 0.12

密度 ISO 1183-1 kg/m³ 1200

松密度 ISO 60 Pellets kg/m³ 660

气体渗透性 b.o. ISO 2556 Carbon dioxide/ 25.4 µm (1 mil) film cm³/(m²*24 h*bar) 16900

气体渗透性 b.o. ISO 2556 Nitrogen/ 100 µm film cm³/(m²*24 h*bar) 120

气体渗透性 b.o. ISO 2556 Carbon dioxide/ 100 µm film cm³/(m²*24 h*bar) 3800

气体渗透性 b.o. ISO 2556 Oxygen/ 100 µm film cm³/(m²*24 h*bar) 650

气体渗透性 b.o. ISO 2556 Nitrogen/ 25.4 µm (1 mil) film cm³/(m²*24 h*bar) 510

气体渗透性 b.o. ISO 2556 Oxygen/ 25.4 µm (1 mil) film cm³/(m²*24 h*bar) 2760

水蒸汽渗透性 ISO 15106-1 23 °C; 85 % RH/ 100 µm film g/(m²*24 h) 15

Makrolon  AL2447 MAS181

MVR (300 °C/1.2 kg) 19 cm3/10 min; Automotive lighting; low viscosity; UV stabilized; easy release; improved static behavior; headlamp lenses for automotive forward lighting

Makrolon  AX2477 ST

MVR (300 °C/1.2 kg) 19 cm3/10 min; low viscosity; UV stabilized; easy release; developed for high-gloss surfaces with highest requirements; for the use in combination with hard coatings

Makrolon  AX2675

MVR (300 °C/1.2 kg) 12 cm3/10 min; medium viscosity; easy release; automotive exterior roof trim + pillar appliques; developed for high-gloss surfaces with highest requirements; for the use in combination with hard coatings

Makrolon  Ai2497 ST

MVR (300 °C/1.2 kg) 19 cm3/10 min; low viscosity; UV stabilized; easy release; Automotive interior grade with specified sensor signal transparency; developed for high-gloss surfaces with highest requirements

Makrolon  Ai2695 ST

MVR (300 °C/1.2 kg) 12 cm3/10 min; medium viscosity; easy release; Automotive interior grade with specified sensor signal transparency; developed for high-gloss surfaces with highest requirements; for the use in combination with hard coatings; for high transmittance applications in the near-infrared range (NIR)