Makrolon AX2675:MVR (300 °C/1.2 kg) 12 cm3/10 min; medium viscosity; easy release; automotive exterior roof trim + pillar appliques; developed for high-gloss surfaces with highest requirements; for the use in combination with hard coatings
塑料
Makrolon® AX2675
材料类型
聚碳酸酯
材料
塑料:光学性能
机械性能:
属性名称 测试标准 测试标准 单位 数值
3.5%应弯时的弯曲应力 ISO 178 2 mm/min MPa 74
Charpy 冲击强度 ISO 179/1eU -30 °C kJ/m² N
Charpy 冲击强度 ISO 179/1eU -60 °C kJ/m² N
Charpy 冲击强度 ISO 179/1eU 23 °C kJ/m² N
Charpy 缺口冲击强度 ISO 21305/based on ISO 179/1eA -30 °C/ 3 mm kJ/m² 16C
Charpy 缺口冲击强度 ISO 21305/based on ISO 179/1eA 23 °C/ 3 mm kJ/m² 70P
Izod 缺口冲击强度 ISO 21305/based on ISO 180/A 23 °C/ 3 mm kJ/m² 70P
Izod 缺口冲击强度 ISO 21305/based on ISO 180/A -30 °C/ 3 mm kJ/m² 14C
Puncture impact properties - maximum force ISO 6603-2 -30 °C N 6100
Puncture impact properties - maximum force ISO 6603-2 23 °C N 5200
名义断裂拉伸应变 ISO 527-1,-2 50 mm/min % > 50
屈服应力 ISO 527-1,-2 50 mm/min MPa 65
屈服应变 ISO 527-1,-2 50 mm/min % 6
弯曲强度 ISO 178 2 mm/min MPa 98
弯曲强度下的弯曲应变 ISO 178 2 mm/min % 7.1
弯曲模量 ISO 178 2 mm/min MPa 2400
抗拉模量 ISO 527-1,-2 1 mm/min MPa 2400
断裂应力 ISO 527-1,-2 50 mm/min MPa 69
断裂应变 b.o. ISO 527-1,-2 50 mm/min % 120
球压硬度 ISO 2039-1 N/mm² 115
穿透能量 ISO 6603-2 -30 °C J 60
穿透能量 ISO 6603-2 23 °C J 55
Makrolon FR6011 RE CQ
medium viscosity; impact modified; UV stabilized; flame retardant; improved chemical resistance compared to standard Makrolon grades; electrical/electronic; housing parts
Makrolon FR6005
polycarbonate; MVR (300 °C/1.2 kg) 9.0 cm3/10 min; medium viscosity; easy release; flame retardant; impact modified; good surface quality; electrical/electronic; housing parts
Makrolon ET UV510 RE
PC/UV absorber concentrate; high viscosity; easy release; very low plate-out; special grade for the coextrusion of Makrolon ET base resins; solid sheet; multi wall sheets / profiles
Makrolon FR6019 CTI
MVR (300 °C/1.2 kg) 13 cm3/10 min; medium viscosity; flame retardant; UL 94V-0/1.5 mm; CTI = 600 V; developed for high voltage application such as electric vehicles and battery packaging; for available colors, please contact us
Makrolon FP2987
high viscosity; MVR (300 °C/1.2 kg) 9.0 cm3/10 min